LATEST UPDATES

Tuesday, 22 March 2016

Comparison between edge and screw dislocation

S.
NO
Edge dislocation
Screw dislocation
1
These dislocations arise due to 
introduction or elimination of an 
extra row of atoms.
A screw dislocation provides for easy 
crystal growth because additional 
atoms and unit cells can be added to 
step of the screw.
2
Tensile, compressive and shear stress 
fields may be present.
Only shear stress field exists.
3
Region of lattice disturbance 
extends along an dislocation line.
Region of lattice disturbance extends 
in two separate planes at right angles 
to each other.
4
Burger’s vector is always perpendicular
to the dislocation line
Burger’s vector is parallel to the 
dislocation line.
5
These dislocation are formed during 
deformation and during crystallisation.
These dislocations are also formed 
during deformation and during 
crystallisation.
6
An edge dislocation (pure) can glide 
and climb
A screw dislocation can glide only.